摘要：49MnVS3非調(diào)質(zhì)鋼(/%:0.47C,0.39Si,0.90Mn,0.016P,0.050S,0.22Cr,0.09V,0.015Ti,0.011Al,0.02Ni)的生產(chǎn)流程為鐵水預(yù)處理-60 t頂?shù)讖?fù)吹轉(zhuǎn)爐-LF處理-VD真空脫氣-220 mm×300 mm坯連鑄-控軋控冷。研究了控軋控冷工藝對(duì)49MnVS3非調(diào)質(zhì)鋼組織和性能的影響。Ф110 mm軋材試驗(yàn)工藝參數(shù):加熱溫度1150~1250℃、開軋溫度1 050℃、終軋溫度850℃、軋后冷卻速度70℃/min、冷卻開始溫度850℃和終止溫度500℃.結(jié)果表明,試驗(yàn)爐次晶粒度提高0.5-1.0級(jí),帶狀組織減輕0.5~1.5級(jí),硬度、強(qiáng)度及塑韌性均有所提升,獲得良好的強(qiáng)韌性匹配。